==Description==
Feldspars are a group of rock-forming tectosilicate minerals which make up as much as 60% of the Earth's crust.<br><br>
Feldspars crystallize from magma in both intrusive and extrusive igneous rocks, as veins, and are also present in many types of metamorphic rock. Rock formed almost entirely of calcic plagioclase feldspar is known as anorthosite. Feldspars are also found in many types of sedimentary rock.<br><br>
In the manufacture of high-class, colourless glass, feldspar should have a maximum of 0.1% Fe<sub>2</sub>O<sub>3</sub> though upto 0.3% is permissible.<br><br>
The word comes from the German "feldt spat", meaning "field spar", "spar" meaning common clevable material - the material dredged up on farm lands during plowing. Most of them are not affected by acid (exception the Ca rich plagioclase - Anorthite). Orthoclase got its name from the Greek phrase meaning "straight fracture", Microcline from a Greek phrase meaning "small incline", and Plagioclase from the Greek phrase meaning "oblique fracture".<br><br>
Feldspar is used as bonding agent along with magnesium oxide, magnesium chloride and other synthetic glue in the manufacture of abrasives, wheels, discs and other shapes. Feldspar comprises a group of minerals containing potassium, sodium, calcium and [[aluminium]] silicates. They are the most common rock-forming minerals. The common feldspar is potassium feldspar, namely, orthoclase (K<sub>2</sub>O, Al<sub>2</sub>O<sub>3</sub>, 6SiO<sub>2</sub>). Sodium feldspar is albite (Na<sub>2</sub>O, Al<sub>2</sub>O</sub>3</sub>, 6SiO<sub>2</sub>) and calcium feldspar is anorthite (CaO, Al<sub>2</sub>O<sub>3</sub>, 2SiO<sub>2</sub>). A variety of crossed, hatched, twinned orthoclase (to be seen under the petrological microscope only) is called microcline. Sodium and calcium feldspars form a somorphous mixture known as plagioclase feldspars.<br><br>
In between sodium and calcium, the other feldspars of the plagioclase series are oligoclase, andesine, labradorite and bytownite. They are composed of suitable proportions of sodium and calcium with an increasing percentage of calcium beginning from mineral oligoclase to bytownite, turning completely into calcium feldspar (anorthite). A rock containing only plagioclase feldspars is called anorthosite.<br><br>
The commercial feldspar is orthoclase. The potassium molecule is replaced by sodium to some extent and hence, orthoclase feldspar usually contains a small percentage of sodium. The composition range of the commercial feldspar varies within the limits of potash, [[soda]] and upto oligoclase.<br><br>
Potash and soda feldspar occur as essential constituents of granite, syenite and gneisses. However, workable deposits are found in pegmatite veins consisting mainly of feldspar, quartz-feldspar veins and also occur with [[mica]] pegmatites. Feldspar is of widespread occurrence and is mined in almost all countries.<br><br>
Feldspar is generally used for three purposes:<br>
* In making the body composition of several types of porcelain, china and [[earthenware]] and also in the preparation of glazes and enamel.
* As an important ingredient in the glass [[sand]] batch.
* As a bonding agent in the manufacture of bonded abrasives like wheels and discs of garnet, [[corundum]], [[emery]] etc.<br>
The glass and ceramic industries are the major consumers of feldspar and account for 95% of the total consumption.<br><br>
In ceramic bodies, the main vitrifying (fluxing) agent is feldspar. The majority of white ware bodies contain good proportions of feldspar. It acts as a flux. In the ceramic industry, the flux is defined as that portion of the body which develops glass phase. This is provided mostly by feldspar. The amount of flux in a ceramic body should be only in such a proportion as to develop the desired amount of vitrification. If excess of flux is added, the fired body becomes very glassy and consequently, brittle.<br><br>
Feldspar is used in varying proportions in porcelain, china and earthenware. Earthenware contains on an average<br><br>
* 12% feldspar
* 25% [[Ball Clay]]
* 28% china-clay
* 35% quartz<br>
This proportion of feldspar varies in different products like:<br>
* Wall tile -5%
* Floor tile -30%
* Statutory porcelain -50%
* Sanitary china and prodelain bodies -30%<br><br>
In the glass industry also, potash feldspar is used in varying proportions. It may contain 10 to 15% of the batch. Feldspar, in this industry, is valued for two purposes, firstly, it acts as a flux and secondly, for [[alumina]] content. Alumina provides the resistance in glass to impact, bendings, and thermal shock.<br><br>
In ceramic bodies, potash feldspar is preferred although [[soda]] feldspar works as a good flux and can be satisfactorily used in developing ceramic bodies. Potash feldspar has p.c.e. value 10, while soda feldspar has 8-9. Anorthite (the calcium feldspar), though it contains twice as much alumina as soda and potash feldspars and also contains lime which is an important ingredient of glass, is not preferred in the glass industry because it is more refractory (p.c.e. 12). Glass industry prefers to use mainly orthoclase (potash feldspar) because it tends the melt to clear glass while albite (soda feldspar) tends the melt to a translucent glass.<br><br>
Feldspar is used as bonding agent along with magnesium oxide, magnesium chloride and other synthetic glue in the manufacture of abrasives, wheels, discs and other shapes. In the preparation of glazes the fine powder of feldspar is mixed with silica powder and a thin slurry is made. The fired up goods are dipped into the slurry and fired again. This imparts glaze to the surface. Some other ingredients are also added to the slurry to impart glaze and lustre. Each pottery factory has its own technique of preparing slurry which is regarded as a trade secret.<br><br>
In the manufacture of high-class, colourless glass, feldspar should have a maximum of 0.1% Fe<sub>2</sub>O<sub>3</sub> though upto 0.3% is permissible. The presence of iron in the batch composition for glass is not liked because its presence, even in very small quantity, tends to colour the glass. The mesh size required is 40-80 BSS in the glass industry. A still finer mesh can be utilized in the ceramic industry. In this industry, a little higher percentage of iron content in feldspar is not objected to. However, in the preparation of white wares feldspar containing below 0.4% Fe<sub>2</sub>O<sub>3</sub> is preferred.<br><br>
Feldspar is also an important constituent for the preparation of white and coloured enamels for metallic and ceramic surfaces. Of late research is being done to utilize feldspar in the production of good quality, white portland [[cement]].<br><br>
In recent years, nepheline syenite has been found as a good substitute for potash feldspar and is being used in an increasing amount in Canada and USA. Nepheline syenite is an igneous rock consisting chiefly of nepheline, microcline and albit.<br><br>

==Application==
Feldspar is a common raw material used in glassmaking, ceramics, and to some extent as a filler and extender in paint, plastics, and rubber. In glassmaking, alumina from feldspar improves product hardness, durability, and resistance to chemical corrosion. In ceramics, the alkalis in feldspar (calcium oxide, potassium oxide, and sodium oxide) act as a flux, lowering the melting temperature of a mixture. Fluxes melt at an early stage in the firing process, forming a glassy matrix that bonds the other components of the system together. In the US, about 66% of feldspar is consumed in glassmaking, including glass containers and glass fiber. Pottery (including electrical insulators, sanitaryware, tableware, and tile) and other uses, such as fillers, accounted for the remainder.
==Shipment / Storage==
Mostly shipped in bulk. Avoid dust formation. Keep container tightly closed. Not classified as dangerous material by DOT. 
May cause eye and skin irritation. Ingestion may cause gastrointestinal irritation, nausea and diarrhea. Long term exposure to high amount of feldspar without the approved dust mask may cause chronic cough, silicosis and cancer.<br><br>
Melting point: 1100-1450°C 
Specific gravity (water=1): 2.60-2.65
Solubility in water: Negligible %
Volatile by vol: Non-Volatile
Boiling point: N/A 
Appearance: White to tan granules and/or powder

See IMSBC Code and applicable MSDS sheet